Product | Basic characteristic | Result | Standard/DoP |
---|---|---|---|
Washbasin | CA – cleanability | Pass | EN 14688:2006 DoP: 400/04/13 |
LR – load resistance | Pass – wall hung washbasins N/A – remaining washbasins | ||
OF – outflow | CL – 25 washbasins with overflow CL – 00 washbasins without overflow | ||
DA – durability | Pass | ||
Shower tray | CA – cleanability | Pass | EN 14527:2006 +A1:2010 DoP 501/07/18 |
DA – durability | Pass | ||
Bathtub | CA – cleanability | Pass | EN 14527:2006 +A1:2010 DoP 402/02/13 |
Property | Standard | Classification/result | Study conducted by | Study method | Classification criteria | Additional classification | Classification |
---|---|---|---|---|---|---|---|
European classification for the reaction to fire behaviour | EN 13501-1:2007 A1:2009 | E – means that the products are able to resist for a short time a small flame, without flame propagation | Construction Technology Institute, member of the European Organisation of Technical Assessment (EOTA). | EN ISO 11925-2L 15 s exposure | Fs ≤ 150 mm 20 s exposure | Flaming droplets/ particles | E |
Product | Property | Standard | Description | Classification/result | Confirming document |
---|---|---|---|---|---|
Washbasins | Resistance to changes of temperature | European Norm EN 14688 | Marmite Mineral Composite underwent testing at a temperature of 70°C and 15°C in 1000 cycles | No defects were established (cracks, scratches, bulges etc.) | LZE03-01224/17/R31NZE |
Resistance to changes of temperature | US norm CSA B45.5-17 IAPMO Z124-201 | Marmite Mineral Composite underwent testing at a temperature of 66°C and 10°C in 500 cycles | No defects were established (cracks, scratches, bulges etc.) | 1200-17012 and 1200-16007-002 | |
Shower trays | Resistance to changes of temperature | European Norm EN 14527 | Marmite Mineral Composite underwent testing at a temperature of 75°C and 12°C in 1000 cycles | No defects were established (cracks, scratches, bulges etc.) | LZE01-01224/17/R31NZE |
Resistance to changes of temperature | US norm CSA B45.5-17 IAPMO Z124-2017 | Marmite Mineral Composite underwent testing at a temperature of 66°C and 10°C in 250 cycles | No defects were established (cracks, scratches, bulges etc.) | 1200-17012 and 1200-16007-002 | |
Bathtubs | Resistance to changes of temperature | European Norm EN 14516 | Marmite Mineral Composite underwent testing at a temperature of 90°C and 12°C and 75°C and 12°C in 100 cycles | No defects were established (cracks, scratches, bulges etc.) | LZE03-01224/17/R31NZE |
Resistance to changes of temperature | US norm CSA B45.517 IAPMO Z124-2017 | Marmite Mineral Composite underwent testing at a temperature of 66°C and 10°C in 250 cycles | No defects were established (cracks, scratches, bulges etc.) | 1200-17012 and 1200-16007-002 |
Type | Reagent | Removal method | Effect | Classification | Confirming document |
---|---|---|---|---|---|
Acids | Acetic acid (CH3COOH) 10% v/v | Deionised water | No discolorations (stains) or damage to the usable surface were established | CE | Testing report no LOW01-1224/11/ R03OWN |
Alkalis | Sodium hydroxide (NaOH) 5% v/v | Deionised water | No discolorations (stains) or damage to the usable surface were established | CE | Testing report no LOW01-1224/11/ R03OWN |
Alcohols | Ethanol (C2H5OH) 70% v/v | Deionised water | No discolorations (stains) or damage to the usable surface were established | CE | Testing report no LOW01-1224/11/ R03OWN |
Bleaching agents | Sodium hypochlorite (NaOCl) 5% of active chlorine (Cl2) | Deionised water | No discolorations (stains) or damage to the usable surface were established | CE | Testing report no LOW01-1224/11/ R03OWN |
Staining agents | Methylene blue 1% m/m | No discolorations (stains) or damage to the usable surface were established | CE | Testing report no LOW01-1224/11/ R03OWN | |
Salts | Sodium chloride (NaCl) 170g/l, diluted with water to 50% | Deionised water | No discolorations (stains) or damage to the usable surface were established | CE | Testing report no LOW01-1224/11/ R03OWN |
Hair dye | Palette Instant color (dark cherry, pomegranate red) | Clean&Shine agent | We were not able to remove the stains using deionised water, nor using an aluminium oxide suspension. Removable only using sandpaper | CE | Testing report no LOW01-1224/11/ R03OWN |
Toothpaste | Colodent with aloe, Colodent super junior, Colgate herbal, Sensodyne, Blend-amed 3D white lux | Deionised water | No discolorations (stains) or damage to the usable surface were established | CE | Testing report no LOW01-1224/11/ R03OWN |
Reagent | Effect | Standard | Result | Confirming document |
---|---|---|---|---|
Black crayon | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Black shoe polish | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Lipstick | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Ink/ink-pot | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Beetroot juice | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Grape juice | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Tea stains | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Cigarette stains | No discolorations (stains) or damage to the usable surface were established | CSA B45.5-11/IAPMO Z124-2011 | Pass | Testing report IAPMO R&T Lab No.: 19641 California |
Norm | Type of a shower tray | Result | Documentation |
---|---|---|---|
VDI 4100 (French norm) | Single mold, installed on marmite Feet | loudness ≤27dB, compliant with the class II. | Report P-BA 280/2017* |
Double mold, installed on Marmite feet | loudness ≤24dB, compliant with the class III. | Report P-BA 281/2017* | |
DIN 4109 (German norm) | Single mold, installed on marmite Feet | Loudness ≤30dB. shower tray appropriate for installation in class- and workrooms, bathrooms and bedrooms. | Report P-BA 280/2017* |
Double mold, installed on Marmite feet | Loudness ≤30dB. shower tray appropriate for installation in class- and workrooms, bathrooms and bedrooms. | Report P-BA 281/2017* |